Products Description
HDPE (High-Density Polyethylene), LLDPE (Linear Low-Density Polyethylene), and LDPE (Low-Density Polyethylene) are all types of geomembranes used in civil engineering projects. Hdpe Lining 1000 Micron is the most widely used and is known for its strength, durability, and resistance to chemicals and UV radiation. LLDPE has a higher flexibility and is more puncture resistant than HDPE, but is less resistant to chemicals. LDPE is the least strong and durable of the three, but is the most flexible and cost-effective. In summary, Hdpe Lining 1000 Micron is preferred for applications that require high strength and durability, LLDPE is best for applications where flexibility and puncture resistance are more important, and LDPE is suitable for less demanding applications where cost is a major factor.
Products Application
Hdpe Pond Liner Geomembrane Application
Aquaculture.
Landfills.
Water Treatment System.
Mining.
Other Applications.
|
Properties |
Test Method |
Test Value |
|||||||||
|
|
|
0.5 mm |
0.75mm |
1.00 mm |
1.25 mm |
1.50 mm |
2.00 mm |
2.50 mm |
3.00 mm |
||
|
Maximum Deviation of thickness |
|
-15% |
-15% |
-15% |
-15% |
-15% |
-15% |
-15% |
-15% |
||
|
Density (min. ave.) |
D 1505/D792 |
0.940 g/cc |
0.940 g/cc
|
0.940 g/cc |
0.940 g/cc |
0.940 g/cc |
0.940 g/cc |
0.940 g/cc |
0.940 g/cc |
||
|
Tensile Properties(min.ave) |
Yield strength
Break strength |
D6693 |
8N/mm |
11 N/mm |
15 N/mm |
18 N/mm |
22 N/mm |
29 N/mm |
37 N/mm |
44 N/mm |
|
|
|
|
|
14N/mm |
20N/mm
|
27 N/mm |
33 N/mm |
40 N/mm |
53N/mm |
67 N/mm |
80 N/mm |
|
|
Yield elongation |
|
12% |
12% |
12% |
12% |
12% |
12% |
12% |
12% |
||
|
Break elongation |
|
700% |
700% |
700% |
700% |
700% |
700% |
700% |
700% |
||
|
Tear Resistance (min. ave.) |
D 1004 |
63 N |
93 N |
125 N |
156 N |
187 N |
249 N |
311 N |
374 N |
||
|
Puncture Resistance (min. ave.) |
D 4833 |
160N |
240N |
320 N |
400 N |
480 N |
640 N |
800 N |
960 N |
||
|
Carbon Black Content (range) |
D 4218 |
2.0-3.0 % |
2.0-3.0 % |
2.0-3.0 % |
2.0-3.0 % |
2.0-3.0 % |
2.0-3.0 % |
2.0-3.0 % |
2.0-3.0 % |
||
|
Oxidative Induction Time (OIT) (min.ave.) Standard OIT |
D 3895 |
100 min. |
100 min. |
100 min. |
100 min. |
100 min. |
100 min. |
100 min. |
100 min. |
||
|
Oven Aging at 85°C Standard OIT (min. ave.) - % retained after 90 days |
D 5721 D 3895 |
55% |
55% |
55% |
55% |
55% |
55% |
55% |
55% |
||
|
UV Resistance High Pressure OIT (min. ave.) - % retained after 1600 hrs |
D 3895 D 5885 |
50% |
50% |
50% |
50% |
50% |
50% |
50% |
50% |
||
Hot Tags: waterproof polyethylene sheet swimming pool plastic liner, China waterproof polyethylene sheet swimming pool plastic liner manufactures, suppliers, factory, HDPE Liner For Heap Leach Pads, HDPE Smooth Geomembrane, HDPE Liner 1 5mm Heap Leach, HDPE Geomembrane Liner, HDPE Lining 1000 Micron, HDPE Liner For Artificial Lake